Aluminum alloys TIG ER5356 Welding jointing
CHEMICAL COMPONET:
| ALLOY(wt%) | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be | S |
| GB/T RULES | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0005 | Margin |
| AWS RULES | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0008 | Margin |
| EXAMPLE VALUE | 0.15 | 0.10 | 0.03 | 0.15 | 5.2 | 0.1 | 0.05 | 0.12 | 0.0003 | Margin |
MECHANICAL PROPERTY:
| PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | Parent metal | ELONGATION(%) | Heat treatment | ||||||
| GB/T RULES | - | - | - | - | - | ||||||
| AWS RULES | - | - | - | - | - | ||||||
| EXAMPLE VALUE | 105 | 205 | 2014-0 | 17 | AW | ||||||
The main component is ALMg5Cr.
k5% magnesium casting and forging aluminum alloy welding or surface surfacing, universal welding material, high strength, good malleability, good corrosion resistance.
Smooth wire feeding, stable arc combustion, splash rarely forming beautiful.
-
Welding materials for aluminum alloys
-
Polypropylene reactor
-
Gansu Lanke Petrochemical -50℃ propane spherical tank project
CHEMICAL COMPONET:
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be | S | |
| GB/T RULES | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0005 | Margin |
| AWS RULES | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0008 | Margin |
| EXAMPLE VALUE | 0.15 | 0.10 | 0.03 | 0.15 | 5.2 | 0.1 | 0.05 | 0.12 | 0.0003 | Margin |
MECHANICAL PROPERTY:
| PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | Parent metal | ELONGATION(%) | Heat treatment | ||||||
| GB/T RULES | - | - | - | - | - | ||||||
| AWS RULES | - | - | - | - | - | ||||||
| EXAMPLE VALUE | 105 | 205 | 2014-0 | 17 | AW | ||||||