High Carbon steels Manual electrode welding stuff
Application & Standard
1. Suitable for welding of carbon steel and corresponding strength of boiler, pipeline, vehicle,
building, bridge and other structures, such as Q235.
2. The standard we met: GB/T5117 E4315, AWS, ISO2560-A:E 35 3 B 2 2, ISO 2560-B: E4315A
J606Fe is a low alloy steel electrode with low hydrogen potassium coating of iron powder. Our company adopts advanced production technology, strictly control the supply of raw materials, processing and production, finished product inspection, after-sales service of every detail. J606Fe electrode produced by the company can be used for both AC and DC, and can be welded in all positions. And obtain extraordinary process and physical properties. It has been exported to the United States, Iraq, South Africa, India and other countries.
Features
1. Low sodium hydrogen electrode with a stable arc, lovely shape, tiny splash, and exquisite ripple.
2. Consistent mechanical characteristics, strong plasticity, impact resistance, and crack resistance.
Generally choose corresponding electrode according to the strength of the steel grade, at the same time also need according to the steel weldability, the transition of parent metal composition, size, shape, groove welding structure and stress concentration factors, such as comprehensive consideration, the weld cooling speed is larger, the higher strength, easy to weld joint cracks of adverse circumstances, often can choose some less than the strength of parent metal electrode, In case of multi-layer welding of thick plate or normalizing treatment after welding, it is necessary to prevent the phenomenon of low weld strength.
Company & Factory
Product composition and mechanical properties introduction
CHEMICAL COMPONET:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| GB/T RULES | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | - | - | ≥0.10 |
| AWS RULES | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | 0.03 | 0.03 | ≥0.10 |
| EXAMPLE VALUE | 0.046 | 1.5 | 0.25 | 0.03 | 2.85 | 0.7 | 0.006 | 0.005 | 0.001 |
MECHANICAL PROPERTY:
| PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | HEATTREAMENT℃xh | IMAPACT VALUE J/℃ | ELONGATION(%) | |||||||||
| GB/T RULES | 670 | 760 | AW | - | 13 | |||||||||
| AWS RULES | 670 | 760 | AW | - | 15 | |||||||||
| EXAMPLE VALUE | 785 | 840 | AW | 90/-40 | 19 | |||||||||
RECOMMENDED WELDING PARAMETERS:
| DIAMETERS SPECIFICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||||
| ELECTRICITY (Amp) | H/W | 80-110 | 100-130 | 130-180 | 180-230 | |||||
| O/W | 50-80 | 90-120 | 130-160 | - | ||||||
NOTE:
H/W: horizontal position welding
O/W: over-head position welding
TYPICAL CASES
Certificates
Product composition and mechanical properties introduction
CHEMICAL COMPONET:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | V |
| GB/T RULES | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | - | - | ≥0.10 |
| AWS RULES | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.50 | ≥0.20 | 0.03 | 0.03 | ≥0.10 |
| EXAMPLE VALUE | 0.046 | 1.5 | 0.25 | 0.03 | 2.85 | 0.7 | 0.006 | 0.005 | 0.001 |
MECHANICAL PROPERTY:
| PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | HEATTREAMENT℃xh | IMAPACT VALUE J/℃ | ELONGATION(%) | |||||||||
| GB/T RULES | 670 | 760 | AW | - | 13 | |||||||||
| AWS RULES | 670 | 760 | AW | - | 15 | |||||||||
| EXAMPLE VALUE | 785 | 840 | AW | 90/-40 | 19 | |||||||||
RECOMMENDED WELDING PARAMETERS:
| DIAMETERS SPECIFICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||||
| ELECTRICITY (Amp) |
H/W | 80-110 | 100-130 | 130-180 | 180-230 | |||||
| O/W | 50-80 | 90-120 | 130-160 | - | ||||||
NOTE:
H/W: horizontal position welding
O/W: over-head position welding