AWS E308L-16 Stainless steels Manual electrode weld fabrication accessories

It can be used to the corrosion resistance of stainless steel structure, such as the 06Cr19Ni9 and 06Cr19Ni11Ti, whose working temperature below 300 ℃; it can also be used for stainless steel structure using under cryogenic temperatures, such as liquid nitrogen container, liquefied natural gas containers, etc.

Item No：: GES-308LT(E308L-16)A002

Suit for:: Stainless Steel

Brand:: JINGLEI

Power supply polarity:: DC+/AC

Certificate authority：: ABS,CCS,DNV/GL,LR

Origin：: China

Size:: 2.0*250/2.6*300/3.2*350/4.0*350/5.0*350

Welding position: AWS E7018-A1 Low-alloy steels Metal powder welding wire Welding accessories

Send email to us

Product Detail

Sepcification

Product Tags

Application&Standard&Note：

1. Suitable for welding of low temperature storage tanks, containers and other -196℃ low temperature equipment, such as SUS304L, etc.
2. The standard we met: GB/T983 E308L-16, AWS A5.4 E308L-16 & A5.4M E308L-16, ISO3581-A:E(19 9 L) R 1 2, ISO3581-B:ES308L-16

Stick Electrodes, AWS Classification E308-16, Material Stainless Steel, Process Stick Welding (SMAW), For Material Type Stainless Steel to Stainless Steel, Welding Current Designation AC, DCEP, For Welding Position Flat, Horizontal, Overhead, Vertical-Up

Features

1. Titanium calcium stainless steel electrode, the main composition is 18% Cr-9%Ni
2. Stable arc, beautiful forming, fine ripples, few splashes, easy de-slagging, good fire resistance of drug skin, good stomatal resistance.
3. Excellent low temperature toughness at -196℃.

When parts and finished products are rectified, the temperature should not be lower than the following:

Low carbon steel material: -20℃;

Low alloy structural steel material: -15℃.

Generally, the allowable welding temperature of welding parts should meet the requirements of Table.

High Carbon steels Solid wire welding accessories

High Carbon steels Manual electrode welding accessories

Company & Factory

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

ALLOY(wt%)	C	Mn	Si	Cr	Ni	Mo	P	S	Cu
GB/T RULES	0.04	0.5-2.5	1.00	18.0-21.0	9.0-12.0	0.75	0.040	0.03	0.75
AWS RULES	0.04	0.5-2.5	1.00	18.0-21.0	9.0-11.0	0.75	0.040	0.03	0.75
EXAMPLE VALUE	0.037	0.85	0.5	18.2	10.7	0.15	0.027	0.005	0.05

MECHANICAL PROPERTY:

PROPERTY	YIELD STRENGTH(MPa)	EXTENSION STRENGTH(MPa)	HEATTREAMENT℃xh	IMAPACT VALUE J/℃	ELONGATION(%)
GB/T RULES	-	510	-	-	30
AWS RULES	-	520	-	-	30
EXAMPLE VALUE	-	560	-	38/-196	42

RECOMMENDED WELDING PARAMETERS:

DIAMETERS SPECIFICATIONS(mm)		2.0*250	2.6*300	3.2*350	4.0*350	5.0*350
ELECTRICITY (Amp)	H/W	50-75	70-95	80-120	110-160	160-190
	O/W	20-50	45-80	70-110	90-135	-

PACKING DETAILES：

SEPCIFICATION	LENGTH	PCS/1KG	WEIGHT/1KG
2.0mm	300mm	79PCS	2KG
2.6mm	300mm	48PCS	2KG
3.2mm	350mm	27PCS	5KG
4.0mm	350mm	16PCS	5KG
5.0mm	350mm	12PCS	5KG

NOTE:
H/W: horizontal position welding
O/W: over-head position welding

Typical Cases

430Mpa Hand Electrode For Low Carbon Steel05

Certificate

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

ALLOY(wt%)	C	Mn	Si	Cr	Ni	Mo	P	S	Cu
GB/T RULES	0.04	0.5-2.5	1.00	18.0-21.0	9.0-12.0	0.75	0.040	0.03	0.75
AWS RULES	0.04	0.5-2.5	1.00	18.0-21.0	9.0-11.0	0.75	0.040	0.03	0.75
EXAMPLE VALUE	0.037	0.85	0.5	18.2	10.7	0.15	0.027	0.005	0.05

MECHANICAL PROPERTY:

PROPERTY	YIELD STRENGTH(MPa)	EXTENSION STRENGTH(MPa)	HEATTREAMENT℃xh	IMAPACT VALUE J/℃	ELONGATION(%)
GB/T RULES	-	510	-	-	30
AWS RULES	-	520	-	-	30
EXAMPLE VALUE	-	560	-	38/-196	42